China Factory Supply Temperature Compensating Devices - 1.1mm Soft Magnetic Alloy FeNi50 Wire for Chokes – TANKII Manufacture and Factory

Factory Supply Temperature Compensating Devices - 1.1mm Soft Magnetic Alloy FeNi50 Wire for Chokes – TANKII

Short Description:

Send email to us

Product Detail

FAQ

Product Tags

Feedback (2)

we are able to supply top quality items, aggressive price and greatest buyer assistance. Our destination is "You come here with difficulty and we offer you a smile to take away" for Nickel Alloy 205 , Heat Treatment Furnaces , Alloy 120 , Encouraged with the fast producing current market on the speedy foodstuff and beverage consumables all around the entire world , We're hunting forward to functioning with partners/clients to create good results together.

Factory Supply Temperature Compensating Devices - 1.1mm Soft Magnetic Alloy FeNi50 Wire for Chokes – TANKII Detail:

1.1mm Soft magnetic alloy 1J50 Wire for Chokes

Item name	1.1mm Soft magnetic alloy 1J50 Wire for Chokes
Conductor	1J50
Item No	50W11B
Condition	Bright,soft
Dimension	1.1mm
Density	8.25g/cm3
Length	1052m/kg
Weight	about 20kg/coil
Package	wooden case
Standard	GB/T 15018-1194

For 1J50,the equivalent in other country Ni50,Alloy 50, E11a, 50H, Hy-Ra49, PB, UNS N14052, ASTM F30,DIN 2.4478,ASTM 753-2 alloy 2
Alloy melting in a vacuum medium, cast into ingots, after hot forging blanks made of sheet metal, and then after hot rolling, pickling, surface treatment, cold rolling into finished products.
1J50 Iron-nickel alloy(about 50% nickel and 48% iron content) is soft magnetic alloys with high magnetic permeability and high saturation magnetic induction

1J50 Application:
It is mainly used in Various transformers, relays, electromagnetic clutches, chokes and magnetic circuit parts cores, pole shoes, earphone diaphragms, earth leakage circuit breakers, relay parts for earth leakage circuit breakers, gas safety valves, magnetic shields used in medium magnetic fields , Gyroscope, automatic synchronization motor, electronic watch micro motor.

Chemical composition%

C	Mn	Si	P	S	Ni	Cu	Fe
≤0.03	0.3-0.6	0.15-0.3	≤0.02	≤0.02	49.0-51.0	≤0.2	Bal.

Mechanical properties under annealing status(20ºC)

Tensile Strength(Mpa)	Elongation(%)	Hardness(HV)
≥530	≥35	≤155

Physical properties

Density (g/cm3)	8.25
Melting point(ºC)	1395-1425
Electrical resistivity at 20ºC	0.45
Saturation magnetostriction coefficient λθ/ 10-6	25
Curie point Tc/ ºC	500

Coefficient of linear expansion(20ºC~200ºC)X10-6/ºC
Grade	20-100ºC	20-200ºC	20-300ºC	20-400ºC	20-500ºC	20-600ºC
1J50	8.9	9.27	9.2	9.2	9.4

The magnetic properties of alloys with high permeability in weak fields
1J50	Initial permeability	Maximum permeability			Coercivity	Saturation magnetic induction intensity
Сold-rolled strip/ sheet. Thickness, mm	μ_0.08/ (mH/m)		μ_m/ (mH/m)	Hc/ (A/m)			B_S/ T
	≥			≤
0.05 mm	2.5		35	20			1.5
0.1~0.19 mm	3.8		43.8	12
0.2~0.34 mm	4.4		56.3	10.4
0.35~1.0 mm	5.0		65	8.8
1.1~2.5 mm	3.8		44.0	12
Bar
8-100 mm	3.1		25.0	24

Form and Dimension:

Colled Rolled Strip	(0.03~0.10)mm x(180~250)mm >(0.10~1.00)mm x(10~250)mm >(1.00~2.50)mm x(100~250)mm
Wire	Φ0.10~Φ6.00mm
Ribbon	(4.50~20.0)mm x(50~250)mm
Bar/Rod	Φ20.0~Φ100.0mm

Product detail pictures:

Related Product Guide:

To create far more benefit for customers is our company philosophy; customer growing is our working chase for Factory Supply Temperature Compensating Devices - 1.1mm Soft Magnetic Alloy FeNi50 Wire for Chokes – TANKII , The product will supply to all over the world, such as: Qatar, Zimbabwe, British, We have advanced production technology, and pursuit innovative in products. At the same time, the good service has enhanced the good reputation. We believe that as long as you understand our product, you must be willing to become partners with us. Looking forward to your inquiry.

180 Alloy

Advance

Alloy 750

Copel

Precision And Vitreous Resistors

The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!