China 1.2mm 1.6mm 2.4mm 3.17mm Aluminum MIG TIG Welding Wire Rod Er4043 Er4047 Er5356 Er5183 Manufacture and Factory

1.2mm 1.6mm 2.4mm 3.17mm Aluminum MIG TIG Welding Wire Rod Er4043 Er4047 Er5356 Er5183

Short Description:

1.2mm 1.6mm 2.4mm 3.17mm Aluminum MIG TIG Welding Wire Rod Er4043 Er4047 Er5356 Er5183

ER4043 5% content of Si, aluminum silicon alloy welding wire, has good fluidity.
It is used for welding forging and casting materials because of low sensitivity to hot cracking.
It is easy to produce brittle Mg2Si in the weld seam during welding, which reduces the plasticity and corrosion resistance of the joint.
The welding is beautiful and bright, the arc is stable, the spatter is small, but after anodizing, the color is different from the base metal.

Extended Length: 10-20mm

Package: 0.5kg/1kg/5kg/7kg

Specification: 0.8~3.2mm

HS Code: 8311300000

Production Capacity: 150ton/Month

Ultimate Strength: 462MPa

Send email to us

Product Detail

FAQ

Product Tags

Standard: AWS A5.10 ER4043	Chemical Composition %
	Si	Fe	Cu		Mn	Zn	Other				AL
Grade ER4043	4.5 - 6.0	≤ 0.80	≤ 0.30		≤ 0.05	≤ 0.10	-				Rest
Type	Spool (MIG)					Tube (TIG)
Specification (MM)	0.8,0.9,1.0,1.2,1.6,2.0					1.6,2.0,2.4,3.2,4.0,5.0
Package	S100/0.5kg S200/2kg S270,S300/6kg-7kg S360/20kg					5kg/box 10kg/box length :1000MM
Mechanical Properties	Fusion Temperature ºC		Electrical IACS	Density g/mm3		Tensile Mpa		Yield Mpa		Elongation %
	575 - 630		42%	2.68		130 - 160		70 - 120		10 - 18
	Diameter(MM)		1.2			1.6			2.0
MIG Welding	Welding Current – A		180 - 300			200 - 400			240 - 450
	Welding Voltage- V		18 - 26			20 - 28			22 - 32
TIG Welding	Diameter (MM)		1.6 - 2.4			2.4 - 4.0			4.0 - 5.0
	Welding Current – A		150 - 250			200 - 320			220 - 400
Application	Recommended for welding 6061 ,6XXX series;3XXXand2XXX series aluminum alloy.
Notice	1,The product can be kept for two years under the condition of factory packing and sealed, and the packing can be removed for three months under the usual atmospheric environment. 2,Products should be stored in a ventilated, dry and place. 3,After the wire is removed from the package, it is recommended that appropriate dust proof cover be applied over the wire.

Almunium alloy welding series:

Item	AWS		Aluminum Alloy Chemical Compostition(%)
Item	AWS		Cu	Si	Fe	Mn	Mg	Cr	Zn	Ti	AL
Pure Aluminum	ER1100		0.05-0.20	1.00		0.05			0.10		99.5
	ER1100		0.05-0.20	1.00		0.05			0.10		99.5	Good plasticity, for gas protective welding or argon arc welding of corrosion resistant pure aluminium.
	Aluminum Alloy	ER5183		0.10	0.40	0.40	0.50-1.0	4.30-5.20	0.05-0.25	0.25	0.15	Rem
High strength, good corrosion resistance, for argon arc welding.
ER5356			0.10	0.25	0.40	0.05-0.20	4.50-5.50	0.05-0.20	0.10	0.06-0.20	Rem
High strength, good corrosion resistance, for argon arc welding.
ER5087			0.05	0.25	0.40	0.70-1.10	4.50-5.20	0.05-0.25	0.25	0.15	Rem
Good corrosion resistance, weldability and plasticity, for gas protective welding or argon arc welding.
ER4047			0.30	11.0-13.0	0.80	0.15	0.10		0.20		Rem
Mainly for brazing and soldering.
ER4043			0.30	4.50-6.00	0.80	0.05	0.05		0.10	0.20	Rem
Good corrosion resistance, wide application, gas protective or argon acr welding.