China 0cr21al4/0cr25al5/0cr19al3 Heating Resistance Wire Fecral Wire Manufacture and Factory

0cr21al4/0cr25al5/0cr19al3 Heating Resistance Wire Fecral Wire

Short Description:

1Cr13Al4 Brand High Temperature Resistance Coil Heater Electric FeCrAl Heating Vape Wire
1Cr13Al4, 0Cr25Al5, 0Cr23Al5, 0Cr21Al6, 0Cr21Al4, 0Cr21Al6Nb, 0Cr27Al7Mo2 is one kind of normal material of Fe-Cr-Al alloy.
FeCrAl alloy has the characteristic of high resistivity,low temperature resistance coefficient,high operating temperature,goodanti-oxidation and anti-corrosion under high temperature.
It is widely used in industrial furnace, household appliances, industry furnace, metallurgy, machinery, aircraft, automotive,
For other industries producing heating elements and resistance elements.

Model NO.: fecral wire

Resistivity: 1.25~1.53 Ω/M

Thermal Conductivity: 46.1 Kj/M.HºC

Maximum Temperature: 1250ºC

Specification: 0.02-7.5mm

Production Capacity: 1000kg Per Week

Send email to us

Product Detail

FAQ

Product Tags

Product Description

Alloy Nomenclature Performance		1Cr13AL4	0Cr25Al5	0Cr21AL6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
	Cr	12.0-15.0	23.0-26.0	19.0-22.0	20.5-23.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.3	3.0-4.2	5.0-7.0	6.0-7.0
Main Chemical composition	Re	opportune	opportune	opportune	opportune	opportune	opportune	opportune
	Fe	Rest	Rest	Rest	Rest	Rest	Rest	Rest
							Nb0.5	Mo1.8-2.2
Max. continuous service temp. of element(ºC)		950	1250	1250	1250	1100	1350	1400
Resistivity at 20ºC(μΩ/m)		1.25	1.42	1.42	1.35	1.23	1.45	1.53
Density(g/cm3)		7.4	7.1	7.16	7.25	7.35	7.1	7.1
Thermal conductivity(KJ/m.h.ºC)		52.7	46.1	63.2	60.2	46.9	46.1	–
Coefficient of lines expansion(α*10-6/ºC)		15.4	16	14.7	15	13.5	16	16
Melting point approx.( ºC)		1450	1500	1500	1500	1500	1510	1520
Tensile strength(N/mm2)		580-680	630-780	630-780	630-780	600-700	650-800	680-830
Elongation at rupture(%)		>16	>12	>12	>12	>12	>12	>10
Variation of area(%)		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Repeat Bending frequency(F/R)		>5	>5	>5	>5	>5	>5	>5
Hardness(H.B.)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
continuous service time(Hours/ ºC)		–	≥80/1300	≥80/1300	≥80/1300	≥80/1250	≥50/1350	≥50/1350
Micrographic structure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic properties		Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic