Cuni10 Copper Nickel Alloy Wire/Sheet/Strip (C70600/Cuprothal 15)

Short Description:

Cuni10 Copper Nickel Alloy Wire/Sheet/Strip (C70600/Cuprothal 15)

Material: CuNi1, CuNi2, CuNi6, CuNi8, CuNi14, CuNi19, CuNi20, CuNi23, CuNi25, CuNi30, CuNi34, CuNi44.
Wire/Rod/Bar diameter: 0.02mm-30mm
Strip: Thickness0.01~6.0width: 610Max
CuNi10, also known as Cuprothal 15, is a copper-nickel alloy (CuNi alloy) with medium-low resistivity for low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F).
CuNi10 is typically used for heating cables, fuses, resistors and various types of controllers.


  • Certificate: ISO 9001
  • Size: Customized
  • Serves: Small Order Accepted
  • Sample: Sample Available
  • standard: GB/ASTM/JIS/BIS/DIN
  • surface: bright
  • type : wire
  • material : copper nickel
  • application: industry
  • treatment : polishing
  • MOQ: 20KG
  • Product Detail

    FAQ

    Product Tags

    Cuni10 Copper Nickel Alloy Wire/Sheet/Strip (C70600/Cuprothal 15)

    Material: CuNi1, CuNi2, CuNi6, CuNi8, CuNi14, CuNi19, CuNi20, CuNi23, CuNi25, CuNi30, CuNi34, CuNi44.
    Wire/Rod/Bar diameter: 0.02mm-30mm
    Strip: Thickness0.01~6.0width: 610Max
    CuNi10, also known as Cuprothal 15, is a copper-nickel alloy (CuNi alloy) with medium-low resistivity for low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F).
    CuNi10 is typically used for heating cables, fuses, resistors and various types of controllers.

    Chemical Content, %

    Ni Mn Fe Si Cu Other ROHS Directive
    Cd Pb Hg Cr
    10 0.3 - - Bal - ND ND ND ND

    Material: CuNi10(C70600) CuNi30(C71500) in from of sheet/plate/strip

    CuNi10Fe1/C70600 Strip/sheet
    Copper Nickels (Copper-Nickel), Copper-Nickel, (90-10). Excellent corrosion resistance, especially in marine environments. Moderately high strength, good creep resistance at elevated temperatures. Properties generally increase with nickel content. Relatively high in cost compared with copper-aluminum and other alloys with similar mechanical propert

    Characteristic Resistivity ( 200C μ Ω . m) Max. working Temperature ( 0C) Tensile Strength (Mpa) Melting point (0C) Density ( g/cm3) TCR x10-6/ 0C (20~600 0C) EMF vs Cu (μ V/ 0C) (0~100 0C)
    Alloy Nomenclature
    NC035(CuNi30) 0.35± 5% 300 350 1150 8.9 < 16 -34

     

    Mechanical Properties Metric Comments
    Tensile Strength, Ultimate 372 – 517 MPa
    Tensile Strength, Yield 88.0 – 483 MPa Depending on temper
    Elongation at Break 45.0 % in 381 mm.
    Modulus of Elasticity 150 GPa
    Poissons Ratio 0.320 Calculated
    Charpy Impact 107 J
    Machinability 20 % UNS C36000 (free-cutting brass) = 100%
    Shear Modulus 57.0 GPa