OCr21AI4 (214),FCHW-2 Fecral Heating Wire for Furnace
OCr21AI4 (214), FCHW-2 FeCrAl Heating Wire for Furnace
0Cr21Al4
General Information
FeCrAl, a family of iron-chromium-aluminum alloys (Kanthal APM, A-1, D and AF etc.) used in a wide range of resistance and high-temperature applications is also used in the form of resistance wires.
Name:heating wire
colour:oxidized or shining
Package: Carton or wooden case as demanded
Application: making heating equipment like industrial furnace, civil heating appliance, various electrical resistors and locomotive braking resistor
Place of Origin: Jiangsu, China (Mainland)
| Designation | Components | |||||||
| Ni | Fe | Zn | Mn | Cu | AI | Cr | Si | |
| NCHW-1 | 77 Min | 2.5 Max | 19~21 | 0.75~1.5 | ||||
| NCHW-2 | 57 Min | 1.5 Max | 15~18 | 0.75~1.5 | ||||
| FCHW-1 | rem | 1.0 Max | 4.0~6.0 | 23~26 | 1.5 Min | |||
| FCHW-2 | rem | 1.0 Max | 2.0~4.0 | 17~22 | 1.5 Min | |||
Usage: Resistor
Size: Thickness 0.01-7mm, width 1mm-1000mm
Surface: BA, 2B
| Alloy material | Chemical composition % | |||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | others | |
| max(≤) | ||||||||||
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.60 | 20.0-23.0 | Rest | ≤0.50 | ≤1.0 | - |
| Cr30Ni70 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.60 | 28.0-31.0 | Rest | ≤0.50 | ≤1.0 | - |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.60 | 15.0-17.0 | 55.0- 61.0 | ≤0.50 | Rest | - |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1 | 1.00-3.00 | 18.0-21.0 | 34.5-36.0 | - | Rest | - |
| Cr20Ni30 | 0.08 | 0.02 | 0.015 | 1 | 1.00-2.00 | 18.0-21.0 | 30.0-31.5 | - | Rest | - |
| 1Cr13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | - | 3.5-4.5 | Rest | - |
| 0Cr15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | - | 4.5-5.3 | Rest | - |
| 0Cr25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | Rest | - |
| 0Cr23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Rest | - |
| 0Cr21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | Rest | - |
| 1Cr20Al3 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 18.0-21.0 | ≤0.60 | 3.0-4.2 | Rest | - |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | Rest | Nb add0.5 |
| 0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.2 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | Rest | |
in the form of wire, ribbon and strip
Wire: 0.018mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Strip: 0.5*5.0mm-5.0*250mm
Packaging & Delivery
| Packaging Details: | plastic film inside , wooden pallets outside , choose the suitable packing, it can be customized by the clients’ demand. |
|---|---|
| Delivery Detail: | about 5-25 days |
WHY CHOOSE US?
All our raw material is made from prime material, not recycle material. We have more than 10 years experience in manufacturing resistance heating alloys.
In the market, not all the NiCr alloys are with standard chemical composition and stable resistance. Professional and reliable is the soul of our business.
1) We achieve consistent production from smelting to complete products, we are able to supply satisfactory products.
2) We have has the world’s advanced level of German ALD - VIDP1000 - 8000KG vacuum induction furnace and wire drawing machines from Japan.
3) With our skilled spooling knowhows, we have successfully magnified the take - up weight on spool. For example, even a superfine wire of 0.04 mm in diameter can be wound and shipped on a 3 - 4 kg bobbin, thus immediately contributing to your productive efficiency.
4) In order to prevent a wire from loosening, we have introduced a developed tension controlled systems into our take - up machine and respooling machine.